Non-aqueous cell having amorphous or semi-crystalline copper manganese oxide cathode material

ABSTRACT

The present disclosure relates generally to a high capacity cathode material suitable for use in a non-aqueous electrochemical cell that comprises copper manganese oxide, which may be in amorphous or semi-crystalline form, and optionally fluorinated carbon. The present disclosure additionally relates to a non-aqueous electrochemical cell comprising such a cathode material and, in particular, to such a non-aqueous electrochemical cell that can deliver a higher capacity than conventional cell.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims priority from U.S. Provisional Patent Application No. 61/112,562 (filed Nov. 7, 2008), No. 61/161,303 (filed Mar. 18, 2009), No. 61/161,300 (filed Mar. 18, 2009), and No. 61/173,534 (filed Apr. 28, 2009), the entire contents of each being incorporated herein by reference.

FIELD OF THE DISCLOSURE

The present disclosure relates generally to a high capacity cathode material suitable for use in a non-aqueous electrochemical cell that comprises an amorphous or semi-crystalline form of copper manganese oxide, and optionally fluorinated carbon. The present disclosure additionally relates to a non-aqueous electrochemical cell comprising such a cathode material and, in particular, to such a non-aqueous electrochemical cell that can deliver a higher capacity than conventional cell.

BACKGROUND OF THE DISCLOSURE

Lithium electrochemical cells, which are more commonly referred to as batteries, are widely used in a variety of military and consumer products. Many of these products utilize high energy and high power batteries. Due in part to the miniaturization of portable electronic devices, it is desirable to develop even smaller lithium batteries with an increased power capability and service life. One way to develop smaller batteries with increased service life is to develop higher energy cathode materials.

One example of a high energy cathode material is fluorinated carbon (i.e., CF_(x)). CF_(x) is often used with a lithium anode in non-rechargeable (primary) batteries for, among other things, military devices and implantable medical devices. CF_(x)(where x=1.0) has a specific energy of about 860 mAh/g. Other examples of high energy cathode materials include silver vanadium oxide and manganese dioxide, which have specific capacities of about 315 and 308 mAh/g, respectively.

The cathodes for rechargeable (secondary) batteries, such as Li ion batteries, generally have lower energy storage capability than primary battery cathodes. However, secondary batteries can typically be recharged several hundred times, which significantly reduces the lifetime cost as well as the battery disposal costs. Examples of secondary battery cathodes used in Li ion batteries include lithium cobalt oxide, lithium iron phosphate, and lithium nickel cobalt oxide.

To satisfy the demands for longer lasting or smaller batteries, there continues to be a need to develop cathodes exhibiting higher energy like primary batteries with the possibility of partial or fully rechargeable capability like secondary batteries, thus extending lifetime and effectively reducing the overall cost. Mixed cathode materials have been proposed as one possible approach for achieving such improved primary and/or secondary batteries. Other benefits of mixed cathode materials include enhancing the rate capability and/or stability of the cathode, while maintaining the energy density per weight and/or per volume. Approaches for achieving such benefits have typically involved mixing a high rate-capable cathode material with a high energy-density cathode material.

U.S. Pat. No. 7,476,467 discloses a cathode material for secondary lithium batteries. The cathode active material comprises a mixture of (A) a lithium manganese-metal composite oxide having a spinel structure. and (B) a lithium nickel-manganese-cobalt composite oxide having a layered structure. The cathode active material is said to have superior safety and a long-term service life at both room temperature and high temperature due to improved properties of lithium and the metal oxide.

It is known to those skilled in the art that composite cathodes comprising fluorinated carbon with some other metal oxide are used for the purpose of providing the battery with an end-of-life (EOL) indicator. For example, U.S. Pat. No. 5,667,916 describes a battery having a cathode mixture of CF_(x) and other materials, including for example copper oxide, the other material or mixtures of other materials serving as the end-of-life indicator. Similarly, U.S. Pat. No. 5,180,642 discloses electrochemical cells or batteries having a cathode mixture comprised of manganese dioxide (MnO₂), carbon monofluoride (CF_(x), where x=1), or mixtures of the two, and an end-of-life additive selected from the group consisting of vanadium oxide, silver vanadate, bismuth fluoride and titanium sulfide. U.S. Pat. No. 4,259,415 provides a cathode material as an end-of-life indicator comprising a main positive active material and a precursor. Suitable main positive active materials include molybdenum oxide (MoO₃), silver oxide (Ag₂O), and graphite fluoride (CF)_(n).

Although many batteries or cells developed to-date include end-of-life indicators, the energy density is less than desired. The capacity (e.g. mAh/gm or mAh/cc) of the EOL additive to CF_(x) (for example, silver vanadium oxide, or SVO) is lower than that of the CF_(x) material, resulting in a composite electrode with a total capacity lower than that of the CF_(x) by itself. Additionally, or alternatively, many batteries or cells developed to-date exhibit an initial voltage sag or drop at the beginning of the discharge. Therefore, a need continues to exist for improved cells, and more particularly for improved cathode materials for use in such cells.

SUMMARY OF THE DISCLOSURE

Briefly, therefore, the present disclosure is directed to a non-aqueous electrochemical cell. The cell comprises: (i) an anode; (ii) a cathode comprising a cathode material comprising copper manganese oxide; (iii) a separator disposed between the anode and the cathode; and, (iv) a non-aqueous electrolyte which is in fluid communication with the anode, the cathode and the separator.

The present disclosure is further directed to such a non-aqueous electrochemical cell wherein the copper manganese oxide has the formula Cu_(a)Mn_(b)O_(c), wherein (i) the copper therein has an oxidation state between about 1 and about 3, (ii) the manganese therein has an oxidation state between about 2 and about 7, (iii) a and b each have a value greater than zero, and further that the sum of a+b is between about 1 and about 3; and, (iv) c has a value greater than zero that may be experimentally determined and that is consistent with the values of a, b and the oxidation states of copper and manganese. More particularly, the present disclosure is directed to such a non-aqueous electrochemical cell wherein copper manganese oxide is amorphous, the copper and manganese being present therein in an average molar ratio of about 1:1 to less than 3:1. Alternatively, the present disclosure is directed to such a non-aqueous electrochemical cell wherein copper manganese oxide is semi-crystalline, the copper and manganese being present therein in an average molar ratio of 3:1 to about 6:1.

The present disclosure is still further directed to one of the foregoing non-aqueous electrochemical cells, wherein the cathode material additionally comprises fluorinated carbon.

The present disclosure is still further directed to one of the foregoing non-aqueous electrochemical cells, wherein the cell is internally rechargeable.

The present disclosure is still further directed to one of the foregoing non-aqueous electrochemical cells, wherein the composition and/or form of the copper manganese oxide, and optionally the ratio thereof relative to fluorinated carbon in the cathode material in the cell, provides an improved end-of-life indicator, as compared to a similarly prepared cathode material in the absence of the copper manganese oxide.

The present disclosure is still further directed to various electronic devices comprising such an electrochemical cell.

It is to be noted that one or more of the additional features detailed below may be incorporated into one or more of the above-noted embodiments, without departing from the scope of the present disclosure.

BRIEF DESCRIPTION OF THE FIGURES

FIG. 1 illustrates a first exemplary test cell for testing various embodiments of the present disclosure.

FIG. 2 illustrates an x-ray diffraction graph according to an embodiment of the copper manganese oxide cathode material of the present disclosure.

FIG. 3 illustrates a discharge voltage profile according to a further embodiment of the copper manganese oxide (Cu_(a)Mn_(b)O_(c)) cathode material of the present disclosure.

FIG. 4 illustrates discharge voltage profiles according to yet another embodiment of the copper manganese oxide (Cu_(a)Mn_(b)O_(c))/CF_(x) (15/85) cathode material of the present disclosure, versus a sample of CF_(x) alone.

FIG. 5 illustrates cyclic voltammograms according to other embodiments of the present disclosure.

FIG. 6 illustrates a lithium CF_(x) discharge profile.

FIG. 7 illustrates a lithium CF_(x) discharge profile.

FIG. 8 is a table showing the density of various Cu_(a)Mn_(b)O_(c) samples, the density being a function of the annealing temperature, according to various embodiments of the disclosure.

FIGS. 9 and 9A illustrate schematic drawings of a coin cell used for testing various alternative embodiments of the present disclosure, FIG. 9A being a schematic cross-section of the cell if FIG. 9 along line 9A.

FIG. 10 illustrates the density of cathode materials formed in accordance with various embodiments of the present disclosure (Cu_(a)Mn_(b)O_(c)), and in particular illustrating the change in density as a function of Cu:Mn molar ratio.

FIG. 11 illustrates an x-ray diffraction graph for cathode materials formed in accordance with various embodiments of the present disclosure, and in particular illustrating the change as a function of Cu:Mn molar ratio.

FIGS. 12A and 12B illustrates Scanning Electron Microscopic images of cathode material formed in accordance with various embodiments of the present disclosure.

FIGS. 13A (XPS-Cu) and 13B (XPS-Mn) illustrates x-ray photon spectroscopic results of cathode materials formed in accordance with various embodiments of the present disclosure.

FIG. 14 illustrates thermal decomposition of cathode materials formed in accordance with various embodiments of the present disclosure, and in particular the change as a function of Cu:Mn molar ratio.

FIG. 15 illustrates a discharge voltage profile of a cell formed according to a further embodiment of the present disclosure (the Cu:Mn molar ratio of the cathode material therein being 3:1).

FIG. 16 illustrates a discharge voltage profile of a cell formed according to yet another embodiment of the present disclosure.

FIG. 17 illustrates a discharge profile of a cell formed according to yet another embodiment of the present disclosure.

FIG. 18 illustrates voltage profiles for ICD testing on LiCF₁, Li/CF_(x), and Li/(CF_(x)+Cu_(a)Mn_(b)O_(c)) cells in accordance with various embodiments of the present disclosure.

DETAILED DESCRIPTION OF THE DISCLOSURE 1. Cathode Material Composition and Cell Components

In accordance with the present disclosure, and as further detailed herein below, it has been discovered that one or more performance properties of a non-aqueous electrochemical cell may be improved or enhanced by the use of a cathode material comprising copper manganese oxide, and more particularly amorphous or semi-crystalline copper manganese oxide. In one particular embodiment of the present disclosure, it has been further discovered that performance of such a non-aqueous cell may be improved or enhanced when copper manganese oxide, and more particularly amorphous or semi-crystalline, is used in combination with fluorinated carbon (i.e., CF_(x)).

In this regard it is to be noted that, as used herein, “non-aqueous” refers to an electrochemical cell that comprises or utilizes an organic solvent, or a mixture of organic solvents, in combination with an inorganic or organic salt, as an electrolyte. Accordingly, the non-aqueous electrolyte contains no added water; that is, water was not added to the electrolyte as a separate or distinct component thereof, but nevertheless may be present as a trace or underlying component or contaminant of the organic solvent(s) used to prepare it. For example, in one or more non-limiting embodiments of the present disclosure, the electrolyte may typically have a water content of less than about 1000 ppm, about 750 ppm, about 500 ppm, about 250 ppm, about 100 ppm, about 50 ppm, about 25 ppm, about 20 ppm, or even less.

In this regard it is to be further noted that an electrochemical cell may otherwise be referred to herein as a battery, a capacitor, a cell, an electrochemical device, or the like. It should be understood that these references are not limiting, and any cell that involves electron transfer between an electrode and an electrolyte is contemplated to be within the scope of the present disclosure.

In this regard it is to be still further noted that “improved” or “enhanced” performance properties generally refers to an improvement or enhancement in the specific energy, the energy density, the operating voltage, the rate capability, and/or the end-of-life behavior or indicator of the non-aqueous electrochemical cell of the present disclosure, as compared for example to a non-aqueous electrochemical cell that is similarly prepared or design but that lacks the copper manganese oxide cathode material as detailed herein.

The copper manganese oxide cathode material of the present disclosure may generally be represented by the formula Cu_(a)Mn_(b)O_(c), and in one or more particular embodiments may be represented by the formula Cu_(a)Mn_(b)O_(c).nH₂O, wherein “nH₂O” represents the structural and/or surface water present in the cathode material. In the cathode material, copper may have an oxidation state between about +1 and about +3, and manganese may have an oxidation state between about +2 and about +7. Additionally, a, b and c each independently have a value of greater than 0, and furthermore (i) the sum of a+b may be in the range of from about 1 to about 3, while (ii) c has a value that may be experimentally determined and that is consistent with the values of a, b and the oxidation states of copper and manganese, and in one or more embodiments is a value such that copper has an oxidation state of approximately +2 or higher.

In this regard it is to be noted that the copper manganese oxide of the present disclosure is not crystalline (e.g., it does not have a spinel-type structure, as is generally known in the art). Rather, the copper manganese oxide of the present disclosure is amorphous, or alternative semi-crystalline, in form. The amorphous or semi-crystalline nature of the material is believed to be, at least in part, a function of the molar ratio of copper to manganese. In particular, among the various embodiments of the present disclosure are those wherein the amorphous copper manganese oxide has the formula Cu_(a)Mn_(b)O_(c), wherein the average molar ratio of Cu to Mn is about 1:1 or more, the ratio for example being between about 1:1 and less than (about) 3:1 (Cu:Mn), or between about 1.25:1 and less than about 2.75:1 (Cu:Mn), or between about 1.5:1 and less than about 2.5:1 (Cu:Mn). In various alternative embodiments, wherein the copper manganese oxide is semi-crystalline and has the formula Cu_(a)Mn_(b)O_(c), the average molar ratio of Cu to Mn is (about) 3:1 or more, the ratio for example being between (about) 3:1 and about 6:1 (Cu:Mn), or between about 3.25:1 and about 5.75:1 (Cu:Mn), or between about 3.5:1 and about 5.5:1 (Cu:Mn).

Additionally, it is to be noted that the amorphous or semi-crystalline copper manganese oxide cathode material of the present disclosure may advantageous having an average density of about 4 g/cm³, about 4.5 g/cm³, about 5 g/cm³, about 5.5 g/cm³, about 6 g/cm³ or more (the density ranging for example from about 4 g/cm³ to about 6 g/cm³, or about 4.5 g/cm³ to about 4.5 g/cm³). Additionally, or alternatively, the cathode material may have a surface area (as determined using means generally known in the art, including for example the BET method) of at least about 50 m²/g, of at least about 75 m²/g, about 100 m²/g, about 125 m²/g, about 150 m²/g, or more, and in one or more embodiments may have a BET surface within the range of, for example, about 50 to about 150 m²/g, or about 75 to about 125 m²/g. In this regard it is to be further noted that the surface area, and thus the ranges related thereto that are noted herein, is a function of the conditions under which the material was prepared, and therefore should not be viewed in a limiting sense.

In addition to the copper manganese oxide cathode material detailed herein, the other components of the non-aqueous electrochemical cell may be selected from among those generally known in the art. For example, according to various embodiments of the present disclosure, the cathode may also include a binder, for example, a polymeric binder such as polytetrafluoroethylene (PTFE) or polyvinylidene fluoride (PVDF), which may optionally be in powdered form. Additionally, carbon materials such as carbon black (e.g., Super P, from Timcal), natural and synthetic graphite, as well as their various derivatives (including graphene, graphite nano platlets, expanded graphite—such as KS4, from Timcal), carbon nano-fibers, and non-graphitic forms of carbon, such as coke, charcoal or activated carbon, may be used as conductive fillers in the cathodes.

In one particular embodiment, however, the cathode material of the present disclosure additionally comprises a carbonaceous active material, and includes graphitic material such as natural and synthetic graphite and all their derivatives including graphene, graphite nano-platelet, expanded graphite, carbon nano-fiber and nongraphitic forms of carbon such as coke, charcoal or activated carbon. In one preferred embodiment, the carbonaceous material is preferably prepared from carbon and fluorine (i.e., it is a fluorinated carbon material). The fluorinated carbon material may generally be represented by the formula (CF_(x))n, wherein x typically varies between about 0.1 to 1.9, preferably between about 0.4 and 1.2, and more preferably between about 0.6 and 1.0. The fluorinated carbon can also be a mixture of (CF_(x1))n and (CF_(x2))m, where x1 is preferably about 0.8 to 1.2, and x2 is preferably about 0.4 to 0.8. In this regard it is to be noted that in the formulas (CF_(x))n and (CF_(x1))n, as well as (CF_(x2))m, n and m refer to the number of monomer units which can vary widely, but may be for example within the range of about 1 to about 5. Accordingly, the ratio of (CF_(x1)) to (CF_(x2)) may be, for example, between about 5:1 and about 1:5, about 4:1 and about 1:4, or about 3:1 and about 1:3, or about 2:1 and about 1:2, or even a ratio of about 1:1; stated another way, the cathode material of the present disclosure, in various embodiments, may contain a mixture of CF_(x), such as for example a mixture of CF₁/CF_(0.6), wherein the mixture has contains for example about 90% CF₁ and about 10% CF_(0.6), or about 80% CF₁ and about 20% CF_(0.6), or about 75% CF₁ and about 25% CF_(0.6), or about 67% CF₁ and about 33% CF_(0.6), or about 50% CF₁ and about 50% CF_(0.6), or vice versa.

It is to be noted that the precise composition of the copper manganese oxide, and/or the precise composition of the fluorinated carbon, and/or the respective concentrations of copper manganese oxide and/or fluorinated carbon, present in the cathode material may be optimized for a given application or use, by means generally known in the art. For example, in one particular embodiment, one or more of these factors may be controlled or optimized in order to improve or enhance the end-of-life behavior of the electrochemical cell. More specifically, one or more of these factors may be controlled or optimized in order to ensure that the electrochemical cell possess or exhibits a voltage plateau after some period of use or discharge, which may act as a useful end-of-life indicator. In this regard it is to be further noted that the discharge voltage of fluorinated carbon is typically between about 2.5 volt (V) and about 2.8V, depending on the discharge rate. In contrast, the copper manganese oxide material of present disclosure exhibits a voltage plateau between about 2 or about 2.3V and about 2.4V, as illustrated for example in FIG. 3.

As used herein, “voltage plateau” generally refers to a portion of the discharge curve that is substantially or relatively flat, within the noted voltage range, for some measurable or detectable period (e.g., over some measurable range of specific capacity values). This voltage plateau is well-suited as end-of-life indicator for a fluorinated carbon/copper manganese oxide non-aqueous electrochemical cell, in accordance with the present disclosure. The amount (i.e., concentration and/or ratio), composition, and/or form of the copper manganese oxide and fluorinated carbon can be optimized to give the desire end-of-life behavior for different applications (the concentrations or ratios of these two cathode materials, for example, having an effect on the specific capacity range at which or over which this plateau is observed).

The respective concentrations of copper manganese oxide and/or fluorinated carbon present in the cathode material may be optimized for a given application or use, by means generally known in the art. In one particular embodiment, however, the cathode mixture of the present disclosure may comprise from between about 1% and about 99%, by weight, of the fluorinated carbon, and in some instances may comprise from between about 10% and about 98%, or about 20% and about 97%, or about 40% and about 96%, or about 60% to about 95%, and in some embodiments may be between about 65% to about 90%, or about 70% to about 85%, by weight. Additionally, the cathode mixture may comprise from between about 1% and about 99%, by weight, of the copper manganese oxide, and in some instances may comprise from between about 2% and about 90%, or about 3% and about 80%, or about 4% and about 60%, or about 5% and about 40%, and in some embodiments may be between about 10% and about 35%, or about 15% and about 30%, by weight. In this regard it is to be noted that, in some embodiment, wherein the cathode material comprises copper manganese oxide and fluorinated carbon, the cathode material may consist essentially of these components; that is, the sum of the concentrations (or weight percents) of the copper manganese oxide and fluorinated carbon may be about 100%. However, in this regard it is to be noted that such concentrations should not be viewed in a limiting sense. For example, in various alternative embodiments, the copper manganese oxide may be the major component of the cathode material (rather than for example the fluorinated carbon).

It is also to be noted that, among the various embodiments of the present disclose, are included those wherein the cathode material is non-lithiated. Stated another way, the cathode material is prepared such that, at least initially (i.e., prior to use), the cathode material is essentially free of lithium or lithium ions therein (i.e., lithium or lithium ions are not intentionally added as a component of the cathode material during preparation). In one particular embodiment, the cathode materials consists essentially of copper manganese oxide, fluorinated carbon, and optionally a binder material and/or a conductive additive (both as further detailed elsewhere herein below). For example, in one preferred embodiment, the cathode material comprises or consists essentially of, by weight, about 81% of the fluorinated carbon and about 12% of the copper manganese oxide, about 3% binder material, and about 4% conductive additive. However, such cathode materials may be utilized in an electrochemical cell with a lithium (Li) anode, for primary (non-rechargeable) or secondary (rechargeable) batteries. As a result, in use, lithium or lithium ions may be present in such a cathode material. The presence of such lithium or lithium ions in use should therefore not be viewed in a limiting sense.

Without being held to any particular theory, it is to be noted that the combination of copper manganese oxide and fluorinated carbon is believed to be particularly advantageous because the combination of these components yields a material having surprisingly higher capacity than expected, based on the individual capacities of the copper manganese oxide and fluorinated carbon. Stated another way, as further illustrated elsewhere herein, the capacity of this mixed cathode material has been observed to be higher than the sum of the individual capacities of the copper manganese oxide and fluorinated carbon alone.

The electrochemical cell of the present disclosure additionally comprises an anode, which may essentially comprise any anode material suitable for use in non-aqueous electrochemical cells. Typically, however, the anode comprises a metal selected from Group IA or Group IIA of the Periodic Table of the Elements, including for example lithium, magnesium, sodium, potassium, etc., and their alloys and intermetallic compounds, including for example Li—Mg, Li—Al, Li—Al—Mg, Li—Si, Li—B and Li—Si—B alloys and intermetallic compounds. The form of the anode may vary, but typically it is made as a thin foil of the anode metal, and a current collector having an extended tab or lead affixed to the anode foil.

As previously noted, the electrochemical cell of the present disclosure further includes a non-aqueous, ionically conductive electrolyte, which serves as a path for migration of ions between the anode and the cathode electrodes during the electrochemical reactions of the cell. The electrolyte can be in either liquid state or solid state, or both. The electrochemical reaction at the electrodes involves conversions of ions in atomic or molecular forms that migrate from the anode to the cathode. Thus, non-aqueous electrolytes suitable for the present disclosure are substantially chemically inert to the anode and cathode materials. Furthermore, a suitable electrolyte in liquid state exhibits those physical properties that are beneficial for ionic transport (e.g., low viscosity, low surface tension, and/or good wettability).

The various components of the electrolyte may be selected from among those generally known in the art, which are suitable for use in combination with the cathode materials detailed elsewhere herein. Preferably, however, a suitable electrolyte for use in accordance with the present disclosure has an inorganic or organic, ionically conductive salt dissolved in a non-aqueous solvent (or solvent system, when a mixture of solvents is used). More preferably, the electrolyte includes an ionizable alkali metal salt dissolved in an aprotic organic solvent or a mixture of solvents comprising a low viscosity solvent and a high permittivity solvent. Without being held to any particular theory, the inorganic, ionically conductive salt is believed to serve as the vehicle for migration of the anode ions to react with the cathode active material. Accordingly, preferably the ion-forming alkali metal salt is similar to the alkali metal comprising the anode.

In one particular embodiment of the present disclosure, for the electrolyte, the ionically conductive salt preferably has the general formula MM′F₆ or MM′F₄, wherein M′ is an alkali metal that is the same as at least one of the metals in the anode and M′ is an element selected from the group consisting of phosphorous, arsenic, antimony and boron. Salts suitable for obtaining the formula M′F₆ include, for example, hexafluorophosphate (PF₆), hexafluoroarsenate (AsF₆) and hexafluoroantimonate (SbF₆), while salts suitable for obtaining the formula M′F₄ include, for example, tetrafluoroborate (BF₄). Alternatively, the corresponding sodium or potassium salts may be used. Thus, for a lithium anode, the alkali metal salt of the electrolyte may optionally be selected from, for example, LiPF₆, LiAsF₆, LiSbF₆ and LiBF₄, as well as mixtures thereof. Other salts that are useful with a lithium anode include, for example, LiClO₄, LiAlCl₄, LiGaCl₄, LiC(SO₂CF₃)₃, LiB(C₆H₄O₂)₂, LiN(CF₃SO₂)₂ and Li(CF₃SO₃), as well as mixtures thereof.

Low-viscosity solvents that may be suitable for use in accordance with the present disclosure in the electrochemical cell include, for example: dimethyl carbonate (DMC), diethyl carbonate, 1,2-dimethoxyethane (DME), tetrahydrofuran (THF), methyl acetate (MA), diglyme, trigylme, tetragylme, and high permittivity solvents, include for example cyclic carbonates, cyclic esters and cyclic amides (such as propylene carbonate (PC), ethylene carbonate (EC), acetonitrile, dimethyl sulfoxide, dimethyl formamide, dimethyl acetamide, gamma-butyrolactone (GBL), and N-methyl-pyrrolidinone (NMP)), as well as various mixtures or combinations thereof.

The type and composition of the solvent used in the electrolyte, and/or the type and concentration of a salt present therein, may be selected in order to optimize one or more physical and/or performance properties of the electrochemical cell of the present disclosure. For example, in one or more embodiments of the present disclosure, the concentration of the salt in the electrolyte may be in the range of from about 0.5M to about 2.5M, or from about 0.75M to about 2.25M, or from about 1M to about 2M. In these or other embodiments of the present disclosure, wherein a mixed solvent system is employed, the ratio (volume) may range for example from between about 1:9 and about 9:1 of a first solvent (e.g., a carbonate solvent, such as propylene carbonate) and a second solvent (e.g., a substituted alkane solvent, such as 1,2-dimethoxyl ethane); that is, the solvent system may comprises from about 10 volume % to about 90 volume %, or from about 20 volume % to about 80 volume %, or from about 30 volume % to about 70 volume %, of a first solvent, all or substantially all of the balance of the solvent system being the second solvent. In one preferred embodiment, however, the anode is lithium metal and the preferred electrolyte is 1.0M to 1.8M LiBF₄ in a mixed PC/DME solvent system (the concentration of the solvent system being between about 10 volume % PC/90 volume % DME and about 70 volume % PC/90 volume % DME).

The electrochemical cell of the present disclosure additionally comprises a suitable separator material, which is selected to separate the cathode/cathode material from the Group IA or IIA anode/anode material, in order to prevent internal short circuit conditions. The separator is typically selected from materials known in the art to be electrically insulating (and sometimes ionically conductive), chemically non-reactive with the anode and cathode active materials, and both chemically non-reactive with and insoluble in the electrolyte. In addition, the separator material is selected such that it has a degree of porosity sufficient to allow flow through of the electrolyte during the electrochemical reaction of the cell. Finally, the separator material is typically selected to have a thickness ranging from, for example, about 15 microns to about 75 microns, or about 20 microns to about 40 microns.

Accordingly, suitable separator materials typically include, or may be selected from, porous or nonporous polymer membranes, such as for example: polypropylene, polyethylene, polyamide (e.g., nylon), polysulfone, polyvinyl chloride (PVC), and similar materials, and combinations thereof (e.g., a trilayer membrane, such as a trilayer membrane of polypropylene/polyethylene/polypropylene), as well as fabrics woven from fluoropolymeric fibers, including for example polyvinylidine fluoride (PVDF), polyvinylidine fluoride-cohydrofluorpropylene (PVDF-HFP), tetrafluoroethylene-ethylene copolymer (PETFE), chlorotrifluoroethylene-ethylene copolymer, and combinations thereof. Fabrics woven from these fluoropolymeric fibers can be used either alone or laminated a microporous film (e.g., a fluoropolymeric microporous film).

The form or configuration of the electrochemical cell of the present disclosure may generally be selected from those known in the art. In one particular embodiment, however, the form or configuration of the electrochemical cell is a case-negative design, wherein the cathode/anode/separator/electrolyte components are enclosed in a conductive metal casing such that the casing is connected to the anode current collector in a case-negative configuration, although case-neutral design is also suitable. A preferred material for the casing is titanium, although stainless steel, nickel, and aluminum are also suitable. The casing header comprises a metallic lid having a sufficient number of openings to accommodate the glass-to-metal seal/terminal pin feed through for the cathode electrode. The anode electrode is preferably connected to the case. An additional opening is provided for electrolyte filling. The casing header comprises elements having compatibility with the other components of the electrochemical cell and is resistant to corrosion. The cell is thereafter filled with the electrolyte solution described hereinabove and hermetically sealed, such as by welding a stainless steel plug over the fill hole. In this regard it is to be noted, however, that the cell of the present disclosure may alternatively be constructed in a case-positive design. Accordingly, the description provided herein should not be viewed in a limiting sense.

In this regard it is to be further noted that other components of the electrochemical cell (e.g., current collectors, etc.) may be selected from among those components generally known in the art, without departing from the scope of the present disclosure.

Once the cathode material has been prepared, it may be deposited on the cathode current collector in the form of single, substantially homogenous mixture (e.g., wherein copper manganese oxide particulate is dispersed into CF_(x) particulate, or vice versa, depending on which is the major component and which is the minor component of the cathode material, and then this mixture is deposited in the form of a single layer on the cathode current collector). Alternatively, however, when a mixture of cathode components or materials are used, these materials may be deposited in the form of layers on (i) the same side of the current collector (e.g., a layer of copper manganese oxide deposited on the surface of the current collector, then a layer of CF_(x) is deposited on the copper manganese oxide layer, or vice versa), or (ii) the opposite sides of the current collector.

It is to be noted that, unless otherwise stated, the various concentrations, concentration ranges, ratios, etc. recited herein, are provided for illustration purposes only and therefore should not be viewed in a limiting sense. It is to be additionally noted that all various combinations and permutations of compositions, concentrations, ratios, components, etc. are intended to be within the scope of and supported by the present disclosure.

2. Cathode Material Preparation

The copper manganese oxide cathode material may be prepared by means generally known in the art, involving for example the chemical reaction of various copper and manganese salts or oxides of both metals, either by solid state reactions or by wet chemistry (including, for example, thermal treatment, sol-gel formation, and hydrothermal synthesis in mixed states).

However, in one or more particular embodiments, the copper manganese oxide material may be prepared in a way that provides or yields the material in an amorphous or semi-crystalline form or state. For example, such copper manganese oxide material may be prepared by a co-precipitation process in the presence or absence of an oxidizing agent, such as potassium persulfate or potassium perchlorate, of copper salts and manganese salts, by a precipitating agent such as potassium hydroxide or sodium carbonate. Alternatively, the cathode material may be the product of the thermal decomposition of copper salts and manganese salts in an appropriate environment. By controlling, for example, the molar ratio of copper to manganese in the starting materials, such that the average molar ratio of copper to manganese in the copper manganese oxide reaction product is within the ranges details herein above, the copper manganese oxide reaction product may be amorphous or semi-crystalline, or a combination or mixture thereof.

Once prepared, the resulting copper manganese oxide may be obtained in the form of particulate (either directly, or after a milling or grinding step of some kind) having an average particle size ranging from about 10 nanometers to about 300 nanometers, or from about 50 nanometers to about 225 nanometers, or from about 80 nanometers to about 150 nanometers. Optionally, the particulate may be agglomerated to form larger particles, having for example an average particle size of ranging from about 5 microns to about 45 microns, or from about 7.5 microns to about 30 microns, or from about 10 microns to about 15 microns.

3. Electrochemical Cell Uses and Performance Properties

It is to be noted that the precise composition of the copper manganese oxide, and/or the cathode material (e.g., mixture of copper manganese oxide with CF_(x)), may be selected to optimize it for a desired performance property, and/or the desired end-use application of the electrochemical cell containing it. Additionally, it is to be noted that it is anticipated within the present disclosure that many other cathode materials may similarly benefit from the addition of Cu_(a)Mn_(b)O_(c), forming a hybrid cathode therewith. Accordingly, references to CF_(x) should not be viewed in a limiting sense.

The cathode material of the present disclosure is generally suitable for use in essentially any non-aqueous electrochemical cell known in the art. Additionally, such an electrochemical cell of the present disclosure, which contains the noted cathode material, is generally suitable for a number of know applications or devices, including for example: medical devices (such as pace makers, defibrillators, cardiac monitors, drug delivery systems, pain management systems, etc.), portable military electronic devices (such as radios, transponders, weapon sights, etc.), marine devices (such as sonobuoys, torpedoes, etc.), aerospace devices (such as deep space probes, command destruct systems, back-up power systems, etc.), military and commercial sensors, remote data collection systems, among other known applications and devices. Such a cathode material, and more specifically the electrochemical cell containing it, may be particularly advantageous for use in devices requiring end-of-life indicators (e.g., medical devices) due to the voltage plateau the cell posses (as further illustrated elsewhere herein below) during the latter portion of the capacity.

In one particular embodiment, the non-aqueous electrochemical cell of the present disclosure may be configured as a reserve battery or cell, whereby the non-aqueous electrolyte is maintained separately from the electrodes, increasing the useful storage period of the battery over a wide temperature range. When needed, the non-aqueous electrolyte and electrodes may be automatically brought into contact, allowing the battery to function in a normal manner.

The cathode materials of the present disclosure, and the non-aqueous electrochemical cells comprising them, may additionally possess one or more other performance properties that are similar to, if not improved or enhanced as compared to, other materials and cells generally known in the art. For example, in various embodiments electrochemical cells or batteries that include a cathode comprising a Cu_(a)Mn_(b)O_(c) cathode material have been observed to exhibit a capacity that is substantially similar to, if not greater than, other high energy cathodes currently in use, such as CF_(x). For example, in one or more embodiments of the present disclosure, the cathode material of the present disclosure may enable such a cell to produce more than about 800, about 900, about 1000, about 1100 milliamp-hours per gram (mAh/g) or greater capacity at room temperature. In comparison to the cathode material of the present disclosure, a cell comprising a CF_(x) cathode material may provide about 820 mAh/g at room temperature. In other various embodiments, however, an electrochemical cell comprising the cathode material of the present disclosure may exhibit improved or enhanced specific energy, energy density, operating voltage, and/or rate capability, as compared for example to conventional non-aqueous electrochemical cells that use cathode materials that do not include copper manganese oxide as the cathode material.

Additionally, and as previously noted, Cu_(a)Mn_(b)O_(c) cathode material may also exhibit increased density compared to other high energy cathodes, and therefore provide a higher energy density than competing materials, such as CF_(x). Exemplary densities of different materials are illustrated in FIGS. 8 and 10. However, it should be appreciated that the density may, in accordance with various aspects, vary depending on the process conditions by which the material was prepared (e.g., annealing temperature).

It is to be further noted that, in another particular embodiment of the present disclosure, the non-aqueous electrochemical cell may exhibit internal charging or rechargeability; that is, the Cu_(a)Mn_(b)O_(c) cathode material of the present disclosure may exhibit the ability to at least partial charge or recharge when used in the non-aqueous electrochemical cell of the present disclosure. Specifically, it has been observed that when electrochemical cells or batteries using such a cathode material, and specifically a cathode material comprising Cu_(a)Mn_(b)O_(c) and CF_(x), were left at open circuit during a life-time test, which took several weeks, the cells exhibited an increasing open cell voltage over time. Furthermore, upon subsequent discharge, the total capacity of the cell exceeded theoretical expectations. Accordingly, the cathode material of the present disclosure exhibited an unexpected benefit, that being an internal recharge behavior without the use of an external power source of any kind.

The potential for at least partial internal charging or internal rechargeability, in addition to the very high primary energy, also makes electrochemical cells or batteries according to embodiments of the present disclosure uniquely-suited, for example, for use in a number of different types of devices. For example, such cells may be well-suited for use in implantable medical devices (e.g., pace makers). Alternatively, such cells may be used in devices designed for both for training and operational situations. An example is military or law enforcement radios that must be used for short periods of time in training, as well as long periods of operational or combat periods. Such devices generally utilize two different types of batteries: short life rechargeable batteries for training, and long life primary batteries for combat. Cu_(a)Mn_(b)O_(c) enhanced batteries may provide a benefit of combining both functions in a single unit, thereby enhancing performance, logistics, and cost savings.

In this regard it is to be noted that, as used herein, “internal charging” or “internal recharging”, as well as variations thereof, generally refers to the ability of the Cu_(a)Mn_(b)O_(c) cathode material, when used in the non-aqueous electrochemical cell of the present disclosure, to recover or re-establish at least a portion of its initial capacity, without the application of an external energy source of some kind to do so.

Without being held to any particular theory, it is believed that the internal charging or recharging mechanism of an electrochemical cell or battery comprising a Cu_(a)Mn_(b)O_(c)/CF_(x) cathode material of the present disclosure may be described by the following set of reactions:

During Discharge Of The Battery:

At the Anode: Li→Li⁺ +e  (1)

At the Cathode (Cu_(a)Mn_(b)O_(c)/CF_(x)/other oxides): CF_(x) +xLi⁺ +xe→C+xLiF  (2) CuO+2Li⁺+2e→Li₂O+Cu  (3) Cu_(a)Mn_(b)O_(c) +nLi⁺ +ne→Li_(n)Cu_(a)Mn_(b)O_(c)  (4) Mn_(b)O_(C) +mLi⁺ +me→Li _(m)Mn_(b)O_(c)  (5)

Self-Charging or Internal Recharging at the cathode: 2LiF+2Cu→CuF₂+2e+2Li⁺  (6) Mn_(b)O_(C) +me+mLi⁺→Li_(m)Mn_(b)O_(c)  (7).

The CuF₂ is an attractive cathode material, which can deliver a specific capacity of about 537 mAh/gm. CuF₂ may be electrochemically formed from LiF and Cu in a non-aqueous electrolyte, through an intermediate, as illustrated below: 4LiF+Cu

Li₂CuF₂+2Li⁺+2e  (8).

It is to be further noted that, in another particular embodiment of the present disclosure, the non-aqueous electrochemical cell may exhibit improved end-of-life behavior. More specifically, in one particular embodiment the composition (e.g., ratio of copper to manganese) and/or form of the copper manganese oxide (e.g., amorphous or semi-crystalline), and optionally the ratio or concentration thereof relative to the fluorinated carbon in the cathode material in the cell, enables the electrochemical cell to possess an improved end-of-life indicator, as compared to a similarly prepared cathode material in the absence of the copper manganese oxide, the cell for example exhibiting, during discharge, a distinct secondary voltage plateau that is less than a first distinct voltage plateau, which acts to single the approaching end-of-life of the cell. Exemplary end-of-life behavior is further illustrated in one or more Examples, below (see, e.g., FIG. 3 and the discussion related thereto).

Having described the disclosure in detail above, it will be apparent that modifications and variations are possible without departing from the scope of the disclosure defined in the appended claims.

The following non-limiting examples are provided to further illustrate the various details and embodiments of the present disclosure.

EXAMPLES Example 1

Cu_(a)Mn_(b)O_(c) was prepared as follows:

CuSO₄.5H₂O (0.25 moles) and MnSO₄.H₂O (0.25 moles) were dissolved in an appropriate amount of deionized water to form a solution. About 100 grams of potassium hydroxide solution (20%) were added drop-wise to the stirred solution of copper and manganese sulfate. The resulting precipitate was collected by filtration and thoroughly washed with deionized water, and dried at 60° C. for about 24 hours. The dried material was then placed in an oven and heated in air at approximately 250° C. for about 15 hours. Finally, the product was ground using mortar and pestle and sieved through a sieve of 60-micron mesh.

Example 2

Cu_(a)Mn_(b)O_(c) was prepared as follows:

CuSO₄.5H₂O (0.05 moles) and MnSO₄.H₂O (0.05 moles) were dissolved in an appropriate amount of deionized water to form a solution. Then, the resulting solution was added drop-wise to stirred solution of 20% KOH containing KClO₄ (0.0125 moles), which is used as an oxidizing agent. When the addition of the solution was completed, the reaction mixture was stirred for about 4 hours. The resulting precipitate was filtered and washed thoroughly and deionized with water. The material was dried at approximately 60° C. for about 24 hours. Prior to being used as a cathode active material, the dried sample was heat-treated at approximately 250° C. for up to 24 to 72 hours, or at about 400° C. for approximately two hours. Optionally, the dried sample may be heat-treated at approximately 250° C. for about 15 hours.

Example 3

CuSO₄.5H₂O (0.05 moles), MnSO₄.H₂O (0.05 moles) and K₂S₂O₈ (0.0125 moles) were dissolved in an appropriate amount of deionized water to form a solution. Then, the resulting solution was added drop wise to a stirred solution of 20% KOH. When the procedure was completed, the precipitate was aged at room temperature in mother liquor for about 4 hours while stirring. The aged precipitate was filtered and washed thoroughly with deionized water. The material was dried at about 60° C. for approximately 24 hours. Prior to being used as a cathode active material, the dried sample was heat-treated at approximately 250° C. for up to 24 to 72 hours, or at about 400° C. for approximately two hours. Optionally, the dried sample may be heat-treated at approximately 250° C. for about 15 hours.

Example 4

Cu_(a)Mn_(b)O_(c) was prepared as follows:

CuSO₄.5H₂O (1.5 moles) and MnSO₄.H₂O (0.25 moles) were dissolved in an appropriate amount of deionized water to form a solution. About 100 grams of potassium hydroxide solution (20%) were added drop-wise to the stirred solution of copper and manganese sulfate. The resulting precipitate was collected by filtration and thoroughly washed with deionized water, and dried at 60° C. for 24 hours. The dried material was then placed in an oven and heated in air at approximately 250° C. for about 15 hours. Finally, the product was ground using mortar and pestle and sieved through a sieve of 60-micron mesh.

It is to be noted that Cu_(a)Mn_(b)O_(c) materials from precursors containing different Cu:Mn molar ratios other than 6:1 can be prepared using the above described method.

Example 5

Cu_(a)Mn_(b)O_(c) was prepared as follows:

CuSO₄.5H₂O (1.5 moles) and MnSO₄.H₂O (0.25 moles) were dissolved in an appropriate amount of deionized water to form a solution. Then, the resulting solution was added drop-wise to stirred solution of 20% KOH containing KClO₄ (0.125 moles), which is used as an oxidizing agent. When the addition of the solution was completed, the reaction mixture was stirred for about 4 hours. The resulting precipitate was filtered and washed thoroughly and deionized with water. The material was dried at approximately 60° C. for 24 hours. Prior to being used as a cathode active material, the dried sample was heat-treated at approximately 250° C. and 400° C. for about 15 and 2 hours, respectively.

It is to be noted that Cu_(a)Mn_(b)O_(c) materials from precursors containing different copper to manganese molar ratios other than 6:1 can be also prepared using the above described method.

Example 6

CuSO₄.5H₂O (1.5 moles), MnSO₄.H₂O (0.25 moles) and K₂S₂O₈ (0.0125 moles) were dissolved in an appropriate amount of deionized water to form a solution. Then, the resulting solution was added drop wise to a stirred solution of 20% KOH. When the procedure was completed, the precipitate was aged at room temperature in mother liquor for about 4 hours while stirring. The aged precipitate was filtered and washed thoroughly with deionized water. The material was dried at about 60° C. for approximately 24 hours. Prior to being used as a cathode active material, the dried sample was heat-treated at approximately 250° C. and 400° C. for about 15 and 2 hours, respectively.

Example 7

CuSO₄.5H₂O (1.5 moles), MnSO₄.H₂O (0.25 moles), C₈H₈O₇ (2 moles) and K₂S₂O₈ (0.0125 moles) were dissolved in an appropriate amount of deionized water to form a solution, which has a pH of about 1.3. Then, 20% KOH solution was added drop wise to the stirred solution until the pH of about 13 was reached, at which point precipitation of product is complete. When the procedure was completed, the precipitate was aged at room temperature in mother liquor for about 45 minutes while stirring. The aged precipitate was filtered and washed thoroughly with deionized water. The material was dried at about 60° C. for approximately 24 hours. Prior to being used as a cathode active material, the dried sample was heat-treated at approximately 250° C. and for about 15 hours. The corresponding copper to manganese molar ratio was 6:1.

Example 8

A sample of Cu_(a)Mn_(b)O_(c) was prepared as set forth in Example 7, except the copper to manganese molar ratio was 5:1 in the mixture solution.

Example 9

A sample of Cu_(a)Mn_(b)O_(c) was prepared as set forth in Example 7, except the copper to manganese molar ratio was 4:1 in the mixture solution.

Example 10

A sample of Cu_(a)Mn_(b)O_(c) was prepared as set forth in Example 7, except the copper to manganese molar ratio was 3:1 in the mixture solution.

Example 11 Test Cell

A first exemplary test cell was constructed to illustrate the characteristics of a cathode that comprises Cu_(a)Mn_(b)O_(c), as prepared in Examples 1-3, above. With reference to FIG. 1, an exemplary test cell comprises a housing X7, an anode X1, a cathode X3, a separator X5 and a non-aqueous electrolyte was prepared. The cell may be used either as a rechargeable or non-rechargeable electrochemical cell. In the cell, the anode X1 was configured to be in electrical contact with a negative lead X2, a cathode X3 was configured to be in electrical contact with a positive lead X4, a separator X5 was configured to electrically separate anode X1 and cathode X3, and an electrolyte permeated the separator X5. Anode X1, cathode X3, separator X5 and the electrolyte were configured to be contained within housing X7. One end of housing X7 was closed with a cap X6, and an annular insulating gasket or O-ring X8 was configured to provide a gas-tight and fluid-tight seal. Positive lead X4 was configured to connect cathode X3 to cap X6.

An electrochemical cell according to various embodiments may be of any configuration, such as a cylindrical wound cell, a button or coin cell, a prismatic cell, a rigid laminar cell or a flexible pouch, envelope or bag cell.

Example 12 Analysis/Testing of Cu_(a)Mn_(b)O_(c) Using Test Cell

X-ray analysis that was performed on a 250° C. heat-treated CuMnO material of Example 3 described above revealed an amorphous structure as illustrated in FIG. 2 (the distinct or sharp peaks or signals at about 30, 36, 38, 44, 54, 58, 64, 68, 72, 76, 76, 81, 84 and 88 being PDF-related peaks). A similar structure was obtained on the sample that was heat-treated at about 400° C. for approximately 2 hours.

The electrochemical behavior of the Cu_(a)Mn_(b)O_(c) of Example 3 was evaluated in a pouch cell, constructed consistent with the details provided above, using lithium metal as an anode. The cathode consisted of 70% Cu_(a)Mn_(b)O_(c) as active material, 14% Super P carbon and 8% KS4 graphite as conductive fillers, and 8% PVDF as binder. Cu_(a)Mn_(b)O_(c), Super P and KS4 were first mixed through ball milling. Then the resulting dry mix was added to a PVDF dissolved in N-methyly-2-pyrrolidene (NMP) solution to form a slurry. Finally, the slurry was applied on a carbon coated aluminum foil substrate to form a cathode, using an electrode coater equipped with an oven to evaporate the NMP.

FIG. 3 shows the discharge profile of the Example 3 Cu_(a)Mn_(b)O_(c) cathode material discussed above in a pouch cell using lithium metal as an anode. The measurements were carried out at room temperature under galvanostic conditions, at a discharge rate of 10 milliamp per gram (mA/g) of cathode active material. The discharge capacity to 1.5 Volts is about 1060 mAh/g. In contrast, as illustrated on FIG. 4, a cell with a CF_(x) electrode exhibits a specific capacity of approximately 860 mAh/g. Thus, the Cu_(a)Mn_(b)O_(c) material of the present disclosure provides an increased specific capacity over devices that include cathodes of CF_(x).

Example 13 End-of-Life Indication

In accordance with various embodiments of the present disclosure, it has been observed that a cathode comprising Cu_(a)Mn_(b)O_(c) may exhibit discharge characteristics that facilitate end-of-life indication. For example, with reference to FIG. 3, after approximately 200 mAh/g, the voltage output of the cell decreased to a second discharge plateau and remained flat at 2.2V to approximately 700 mAh/g. This second plateau may advantageously be used in accordance with various aspects of the present disclosure to detect the end-of-life of the battery, for example when the cell is approaching the end of the discharge process. Such an end-of-life indication may be desirable in medical device applications where it may be desirable to surgically remove a medical device before the battery reaches the end of its lifetime, but not too early during its lifetime.

Example 14 Rechargeable Battery

In still other embodiments, Cu_(a)Mn_(b)O_(c) may exhibit at least partial rechargeability and/or reversibility. FIG. 5 shows cyclic voltammograms of a Cu_(a)Mn_(b)O_(c) cathode in a pouch cell, indicating good reversibility of the cathode over approximately 4.0V to 2.5V. With reference back to FIG. 3, exemplary embodiments of the present disclosure that comprise a Cu_(a)Mn_(b)O_(c) cathode may be reversible during the first approximately 200 mAh/g of capacity. Thereafter, exemplary batteries may still comprise a capacity that is substantially similar to electrodes that comprise CF_(x).

Example 15 Electrodes with Cu_(a)Mn_(b)O_(c) and CF_(x)

As previously noted, in one particular embodiment of the present disclosure, the cathode material may comprise Cu_(a)Mn_(b)O_(c) combined with one or more other cathode materials that have high specific capacity, such as fluorinated carbon (e.g., CF_(x)). A battery with a cathode that comprises Cu_(a)Mn_(b)O_(c) and CF_(x) may exhibit enhanced electrochemical performance (e.g., specific energy, energy density, operating voltage, and rate capability) relative to a battery with CF_(x) alone. Such a battery may also exhibit a more predictable voltage change during the last portion of its capacity, thereby producing a reliable indicator of the end of its useful life.

In a particular embodiment, Cu_(a)Mn_(b)O_(c) formed according to Example 3 above was mixed with fluorinated carbon, and more specifically CF_(x) (having the composition CF₁/CF_(0.6), in the ratio of 80/20) to form a cathode. The cathode active part of the blend consisting of 85% (by weight) carbon fluoride and 15% (by weight) Cu_(a)Mn_(b)O_(c) were mixed with Super P and KS4.

The discharge profile of the cell built with the cathode prepared from the noted cathode mixture at a discharge rate of 10 mA/g is illustrated in FIG. 4. Discharge data for cells built with carbon fluoride alone as active are provided in FIG. 4 for comparison. The specific capacity to 1.5 Volts of cells built with the admixture of carbon fluoride and Cu_(a)Mn_(b)O_(c) as cathode materials is about 1100 mAh/g. When evaluated alone, carbon fluoride based cells delivered a specific capacity to 1.5 Volts of about 820 mAh/g.

It is to be noted that the mixture of 85% CF_(x), having an expected capacity of 704 mAh/g, and 15% Cu_(a)Mn_(b)O_(c), having an expected capacity of 1060 mAh/g, should have produced a hybrid cathode delivering a capacity of about 810 mAh/g. The new cathode instead produced an unexpected 36% greater capacity of 1100 mAh/g. The incorporation of the Cu_(a)Mn_(b)O_(c) according to embodiments of the present disclosure into carbon fluoride (or more generally fluorinated carbon) thus led to cells with about 56% capacity improvement, as compared to cells built with carbon fluoride alone as cathode active materials.

Example 16 Test Cell

A second exemplary test cell was constructed to further illustrate the characteristics of a cathode that comprises Cu_(a)Mn_(b)O_(c), as prepared in Examples 4-10, above. Specifically, an exemplary coin cell battery, illustrated in FIGS. 9 and 9A, was used as test vehicle (unless otherwise mentioned) to evaluate the discharge characteristics of a cathode that comprises Cu_(a)Mn_(b)O_(c). With reference to FIGS. 9 and 9A (FIG. 9A being a cross-section of FIG. 9, along the 9A line), an exemplary test cell comprised a cell can (Y1), a cathode (Y2), a separator (Y3), a non-aqueous electrolyte, a stainless steel spacer (Y4), a gasket (Y5), a Belleville spring (Y6), a cell cap (Y7) and an anode (Y8). The cell was used either as a rechargeable or non-rechargeable electrochemical cell. Anode, cathode, separator and the electrolyte were configured to be contained within cell can and cell cap.

Other electrochemical cells according to various embodiments may be of any configuration, such as a cylindrical wound cell, a prismatic cell, a rigid laminar cell or a flexible pouch, envelope or bag cell.

Example 17 Analysis/Testing of Cu_(a)Mn_(b)O_(c) Using Test Cell

Density measurements for Cu_(a)Mn_(b)O_(c) are shown in FIG. 10. The density of exemplary copper manganese oxide material was found to be between about 4.2 to about 5.5 g/cm³. X-ray patterns of 250° C. heat-treated materials of Examples 7, 8, 9 and 10 are illustrated in FIG. 11. As can be seen, there are essentially no sharp peaks characteristic of crystalline materials. However, two small peaks attributable to CuO were observed for the sample prepared using Example 8. The XRD patterns of samples prepared by Examples 8, 9, and 10 exhibited a small peak, tentatively attributable to Cu₂O. The semi-crystalline nature of the materials of the present disclosure typically occurs with higher copper content (e.g., 6:1 molar ratio of Cu:Mn). When a low copper content is used (e.g., 1:1 Cu:Mn molar ratio), the resulting material is essentially amorphous, as revealed by XRD.

The surface area of this material was measured by BET method and found to be about 70 m²/g. Scanning Electron Microscopic images in FIG. 12A illustrate the particles are in micron size; however, the higher magnification image (insert in FIG. 12A) reveals the nano sized particles are agglomerated and form micron size particles. The agglomerated particles produce a more “pore-like” structure with a high surface area. FIG. 12B illustrates a SEM image showing two different features of the surfaces, which are likely to originate from two different components. One component is highly electrically conductive, which is CuO, is darker (arrow indicated in FIG. 12B) and the low conductive component is likely an amorphous form of manganese oxide and/or copper manganese oxides, which are brighter in the illustrated image due to their less conductive nature.

FIGS. 13A and 13B illustrates the X-ray Photon Spectroscopy (XPS) results of a sample formed in accordance with Example 7. The detailed peak analysis of Cu shows two peaks at 934.1 eV and 954.0 eV, attributable to the characteristic binding energy of CuO and Cu_(a)Mn_(b)O_(c), respectively. Further, the analysis of manganese element shows binding energy peaks at 642.8 and 654.1 eV, belonging to manganese (IV) oxide (MnO2). The large shoulder in the Mn peak may be due to part of the materials being in a high oxidation state. The calculated metal to oxygen ratio is 0.44, for example; it is well known that metal to oxygen ratio of Cu_(a)Mn_(b)O_(c) spinel is 0.6 and CuO/MnO₂ is 0.5. These results suggest that this compound is likely in higher oxidation state than spinel form of Cu_(a)Mn_(b)O_(c).

In the illustrated cases, the XRD results show that CuO is a semi- and/or crystalline material, whereas manganese oxide and copper manganese oxide are amorphous. XPS and elemental analysis confirms the composition of the materials, which contains Cu, Mn and O. The detailed elemental scan by XPS further indicates the presence of CuO, MnO₂ and Cu_(a)Mn_(b)O_(c). High magnification SEM images show the presence of different elements in the sample. These results suggest that the material of the present disclosure exhibits an amorphous and/or a semi-crystalline nature.

FIG. 14 shows the thermal decomposition of copper manganese oxides synthesized using different molar ratios. The thermal decomposition was performed in air at the heating rate of 10° C./min. FIG. 14 shows that all these materials are thermally stable at 500° C., and the observed weight loss was about 4%, which can be attributed to surface or crystalline water. When stored, the cathode (made up of the cathode material of the present disclosure) in electrolyte (PC/DME/LiBF₄) at 60° C. for 22 days, the average dissolved amount of Cu and Mn is about 5 ppm and 1 ppm, respectively. This data demonstrates good chemical and thermal stability of the materials of various embodiments of the present disclosure.

Electrochemical behavior of the cathode material in accordance with various embodiments of this disclosure was evaluated in 2325 size coin cell using lithium metal as an anode. The cathode consisted of 70% Cu_(a)Mn_(b)O_(c) as the active material, 27% KS4 graphite as conductive fillers, and 3% PTFE as binder. Cu_(a)Mn_(b)O_(c) and KS4 were first mixed using a mortar and pestle. Then PTFE powder was added to the resulting mix while mixing to form a cathode sheet. The electrode was cut from the resulting sheet with a die. Prior to testing in 2325 size coin cells, the cathodes were vacuum dried at 120° C. for about 4 hours.

FIG. 15 shows the discharge profile of the cathode materials of Example 10 in a coin cell using lithium metal as an anode. The electrochemical performance was measured using a Maccor battery testing system. The first discharge of the cell was at 10 mA/g, down to 2.6 Volts, the second at 5 mA/g down to 2.3 Volts, and the third 1 mA/g down to 1.5 Volts (signature test). Thus, Cu_(a)Mn_(b)O_(c), according to various embodiments, exhibited a specific capacity of about 900 mAh/g to about 2 Volts, with a plateau to about 2.4 Volts.

In a further embodiment, Cu_(a)Mn_(b)O_(c), was mixed with carbon fluoride (CF₁/CF_(0.6) in the ratio of about 80/20) to form a cathode. The cathode active part of the blend, which included about 90% (by weight) carbon fluoride and 10% (by weight) Cu_(a)Mn_(b)O_(c), was mixed with carbon black and graphite. (All percents set forth herein are in weight percents, unless otherwise noted.) The investigated cathode was prepared as described herein above. The discharge profile of the cell built with the resulting cathode, at a discharge rate of 10 mA/g, is illustrated in FIG. 16. Discharge data for cells built with carbon fluoride alone as active are provided in FIG. 16 for comparison. The specific capacity to 1.5 Volts of cells built with the admixture of carbon fluoride and Cu_(a)Mn_(b)O_(c), in accordance with the present disclosure, as cathode materials is about 1007 mAh/g. When evaluated alone, carbon fluoride based cells delivered a specific capacity to 1.5 Volts of about 820 mAh/g.

It is to be noted that the mixture of 90% CF_(x), having an expected capacity of about 746 mAh/g, and 10% Cu_(a)Mn_(b)O_(c), having an expected capacity of about 1000 mAh/g, would be expected to produce a hybrid cathode delivering a capacity of about 846 mAh/g. However, the new cathode produced an unexpected value of about 19% greater capacity at about 1007 mAh/g. Thus, the incorporation of the Cu_(a)Mn_(b)O_(c) into carbon fluoride, according to various embodiments of the present disclosure, thus led to cells with about 35% capacity improvement as compared to cells built with carbon fluoride alone as cathode active materials.

Example 18 Internally Rechargeable Battery

As previously noted, cells comprising CF_(x) and the copper manganese mixed oxide of the present disclosure have been observed to exhibit a self-charging capability (i.e., an internal charging or recharging capability). Without being held to any particular theory, it is believed that this is due at least in part to redox reactions involving the discharge products within the cathode as previously discussed above. FIG. 17 shows the discharge behavior at 3 mA/g of the cell after 5 cycles of self-charging. Note that the cell was first discharged using a signature test (i.e., 10 mA/g to 2.5 Volts, 30 mA/g to 2.0 Volts and then at 1 mA/g). It was then taken out of testing and allowed to rest for about 5 days prior to discharging. While resting, the cell OCV rose from about 1.7 Volts to about 2.9 Volts, which suggests an internal- or self-charging process.

FIG. 18 illustrates the voltage profile on ICD test of a pouch cell comprising CF_(x) and the cathode materials of the present disclosure, Cu_(a)Mn_(b)O_(c). The cathode comprised about 90% CF_(x) and about 10% Cu_(a)Mn_(b)O_(c), by weight. The discharge protocol was as follows: there were four pulses per train in every four hours. The pulse amplitude was calculated by 0.7 A per gram of active materials. As shown in FIG. 18, the voltage dip for the first train of pulses was lessened or eliminated by incorporating the Cu_(a)Mn_(b)O_(c) material of the present disclosure into the cathode. This result suggests that the cell comprising CF_(x) and the cathode of the present disclosure has a good rate capability at early stage of discharge compared to cell comprising CF_(x) without Cu_(a)Mn_(b)O_(c).

When introducing elements of the present disclosure or the preferred embodiments(s) thereof, the articles “a”, “an”, “the” and “said” are intended to mean that there are one or more of the elements. The terms “comprising”, “including” and “having” are intended to be inclusive and mean that there may be additional elements other than the listed elements.

As various changes could be made in the above-described embodiments (e.g., cathode material compositions, electrochemical cell components and configurations, etc.) without departing from the scope of the disclosure, it is intended that all matter contained in the above description and shown in the accompanying figures shall be interpreted as illustrative and not in a limiting sense. 

What is claimed is:
 1. A non-aqueous electrochemical cell comprising: an anode; a cathode comprising a cathode material comprising: an amorphous or semi-crystalline copper manganese oxide cathode material; and fluorinated carbon; a separator disposed between the anode and the cathode; and a non-aqueous electrolyte which is in fluid communication with the anode, the cathode, and the separator, wherein: the copper manganese oxide cathode material has an average density ranging from about 4.5 to about 5.5 g/cm³.
 2. The non-aqueous electrochemical cell of claim 1, wherein the amorphous or semi-crystalline copper manganese oxide cathode material has the formula Cu_(a)Mn_(b)O_(c), wherein: (i) the copper therein has an oxidation state between about 1 and about 3, (ii) the manganese therein has an oxidation state between about 2 and about 7, (iii) a and b each have a value greater than zero, (iv) the sum of a+b is between about 1 and about 3; and (v) c has a value that may be experimentally determined and that is consistent with the values of a, b, and the oxidation states of copper and manganese.
 3. The non-aqueous electrochemical cell of claim 1, wherein the amorphous or semi-crystalline copper manganese oxide cathode material has the formula Cu_(a)Mn_(b)O.nH₂0, wherein: (i) the copper therein has an oxidation state between about 1 and about 3, (ii) the manganese therein has an oxidation state between about 2 and about 7, (iii) a and b each have a value greater than zero, (iv) the sum of a+b is between about 1 and about 3; (v) x has a value that may be experimentally determined and that is consistent with the values of a, b and the oxidation states of copper and manganese; and (vi) nH₂O represents the surface water, the structural water, or both, present in the copper manganese oxide cathode material.
 4. The non-aqueous electrochemical cell of claim 1, wherein the copper manganese oxide cathode material has an average BET surface area ranging from about 50 to about 150 m²/g.
 5. The non-aqueous electrochemical cell of claim 1, wherein the copper manganese oxide cathode material has an average BET surface area ranging from about 75 to about 125 m²/g.
 6. The non-aqueous electrochemical cell of claim 1, wherein the copper manganese oxide cathode material has an average particle size ranging from about 10 to about 300 nanometers.
 7. The non-aqueous electrochemical cell of claim 1, wherein the copper manganese oxide cathode material is amorphous, the copper and manganese being present therein in an average molar ratio of from about 1.5:1 to about 2.5:1 (Cu:Mn).
 8. The non-aqueous electrochemical cell of claim 1, wherein the copper manganese oxide cathode material is semi-crystalline, the copper and manganese being present therein in an average molar ratio of 3:1 to about 6:1 (Cu:Mn).
 9. The non-aqueous electrochemical cell of claim 1, wherein the copper manganese oxide cathode material is in a form of agglomerated particles, the agglomerated particles having an average agglomerated particle size of from about 5 to about 45 microns.
 10. The non-aqueous electrochemical cell of claim 1, wherein the fluorinated carbon has the formula CF_(x), wherein x is about 0.1 to about 1.9.
 11. The non-aqueous electrochemical cell of claim 10, wherein: a concentration of copper manganese oxide in the cathode material is between about 1 wt % and about 99 wt %, and a concentration of fluorinated carbon in the cathode material is between about 99 wt % and about 1 wt %.
 12. The non-aqueous electrochemical cell of claim 1, wherein the fluorinated carbon is a mixture of materials having the formulas (CF_(x1))n and (CF_(x2))m, wherein: x1 is about 0.8 to about 1.2, x2 is about 0.4 to about 0.8, n is about 1 to about 5 m is about 1 to about 5, and (CF_(x1))n and (CF_(x2))n are not the same.
 13. The non-aqueous electrochemical cell of claim 12, wherein: a concentration of copper manganese oxide in the cathode material is between about 1 wt % and about 99 wt %, and a concentration of fluorinated carbon in the cathode material is between about 99 wt % and about 1 wt %.
 14. The non-aqueous electrochemical cell of claim 1, wherein the non-aqueous electrolyte comprises an organic solvent selected from the group consisting of dimethyl carbonate (DMC), diethyl carbonate, 1,2-dimethoxyethane (DME), tetrahydrofuran (THF), methyl acetate (MA), diglyme, trigylme, tetragylme, propylene carbonate (PC), ethylene carbonate (EC), acetonitrile, dimethyl sulfoxide, dimethyl formamide, dimethyl acetamide, gamma-butyrolactone (GBL), and N-methyl-pyrrolidinone (NMP), and a mixture of two or more thereof.
 15. The non-aqueous electrochemical cell of claim 14, wherein the non-aqueous electrolyte comprises a salt having a formula MM′F₆ or MM′F₄, wherein: M is an alkali metal that is the same as at least one metal present in the anode, and M′ is an element selected from the group consisting of phosphorous, arsenic, antimony, and boron.
 16. The non-aqueous electrochemical cell of claim 15, wherein the salt is selected from the group consisting of LiPF₆, LiAsF₆, LiSbF₆, LiBF₄, LiClO₄, LiAlCl₄, LiGaCl₄, LiC(SO₂CF₃)₃, LiB(C₆H₄O₂)₂, LiN(CF₃SO₂)₂, Li(CF₃SO₃), and mixtures thereof.
 17. The non-aqueous electrochemical cell of claim 15, wherein a concentration of the salt in the organic solvent is in a range of between about 0.5 M and about 2.5 M.
 18. The non-aqueous electrochemical cell of claim 1, wherein the anode comprises a metal selected from Group IA or Group IIA of the Periodic Table of the Elements.
 19. The non-aqueous electrochemical cell of claim 18, wherein the anode comprises a metal selected from the group consisting of lithium, magnesium, sodium, and potassium.
 20. The non-aqueous electrochemical cell of claim 19, wherein the anode comprises an alloy or an intermetallic compound selected from the group consisting of Li—Mg, Li—Al, Li—Al—Mg, Li—Si, Li—B, and Li—Si—B.
 21. The non-aqueous electrochemical cell of claim 1, wherein: the cathode material additionally comprises fluorinated carbon, and the cell exhibits an end-of-life indication comprising a voltage plateau of about 2 to about 2.4 volts. 